Efficient, stable, and eco-friendly thermoelectric material discovered

Xi Zhang, Yuqiao Zhang*, Liao Wu, Akihiro Tsuruta, Masashi Mikami, Hai Jun Cho, and Hiromichi Ohta*, “Ba1/3CoO2: A Thermoelectric Oxide Showing a Reliable ZT of ∼0.55 at 600 °C in Air”, ACS Appl. Mater. Interfaces XX, XXXX (2022). (DOI: 10.1021/acsami.2c08555)

The crystal structure of the barium cobalt oxide and the film itself

Waste heat is a very promising source of energy conservation and reuse, by means of converting this heat into electricity—a process called thermoelectric conversion. Commercially available thermoelectric conversion devices are synthesized using rare metals. While these are quite efficient, they are expensive and, in the majority of cases, utilize toxic materials. Both these factors have led to these converters being of limited use. One of the alternatives are oxide-based thermoelectric materials, but the primary drawback these suffer from is a lack of evidence of their stability at high temperatures.

A team led by Professor Hiromichi Ohta at the Research Institute for Electronic Science at Hokkaido University has synthesised a barium cobalt oxide thermoelectric converter that is reproducibly stable and efficient at temperatures as high as 600°C. Their findings were published in the journal ACS Applied Materials & Interfaces.

Thermoelectric conversion is driven by the Seebeck effect: when there is a temperature difference across a conducting material, an electric current is generated. However, efficiency of thermoelectric conversion is dependent on a figure called the thermoelectric figure of merit ZT. Historically, oxide-based converters had a low ZT, but recent research has revealed many candidates that have high ZT, but their stability at high temperatures was not well documented.

Hiromichi Ohta’s group has been working on layered cobalt oxide films for over two decades. In this study, the team sought to examine the thermal and chemical stability of these films, as well as measure their ZT values, at high temperatures. They tested cobalt oxide films layered with sodium, calcium, strontium or barium, analysing their structure, resistivity, and thermal conductivity.

(Left) ZT of all four cobalt oxide films increases with increasing temperature. The barium cobalt oxide film (red diamonds) has the highest ZT among the four, reaching a high ZT value of ~0.55 at 600 °C. (Right) The ZT of the barium cobalt oxide film at 600 °C is comparable to that of commercially available thermoelectric converters (lead-tellurium, PbTe, and silicon germanium, SiGe; Xi Zhang, Yuqiao Zhang, et al. ACS Applied Materials & Interfaces. July 12, 2022).

They found that, of the four variants, the barium cobalt oxide layered film retained its stability in terms of structural integrity and electrical resistivity at temperatures as high as 600°C. In comparison, the sodium- and calcium cobalt oxide films were only stable until 350°C, and the strontium cobalt oxide film was stable up to 450°C. The ZT of the barium cobalt oxide film increased with the temperature, reaching ~0.55 at 600°C, comparable to some commercially available thermoelectric converters.

“Our study has shown that barium cobalt oxide films would be excellent candidates for high-temperature thermoelectric conversion devices,” said Hiromichi Ohta. “ In addition, they are environment friendly, giving potential for wide deployment.”

Hiromichi Ohta’s research group at RIES, Hokkaido University. Hiromichi Ohta, Xi Zhang, Liao Wu, Hai Jun Cho and Yuqiao Zhang contributed to the current study (Photo: Hiromichi Ohta).

Original Article:

Xi Zhang, Yuqiao Zhang, et al. Ba1/3CoO2: A Thermoelectric Oxide Showing a Reliable ZT of ~0.55 at 600 °C in AirACS Applied Materials & Interfaces. July 12, 2022.

DOI: 10.1021/acsami.2c08555 (Open Access)

Funding:

This work was supported by the Japan Society for the Promotion of Science (JSPS) Grants-in-Aid for Innovative Areas (19H05788) and Grant-in-Aid for Scientific Research A (22H00253).

Contacts:

Professor Hiromichi Ohta

Research Institute for Electronic Science

Hokkaido University

Tel: +81-11-706-9428

Email: hiromichi.ohta[at]es.hokudai.ac.jp

Sohail Keegan Pinto (International Public Relations Specialist)

Public Relations Division

Hokkaido University

Tel: +81-11-706-2185

Email: en-press[at]general.hokudai.ac.jp